Dimensional effect during martensitic transformation in splat cooled Ti Ni Cu ( at. %) alloysV. A. Lobodyuk
Department of Phase Transformations, G.V. Kurdyumov Institute for Metal Physics of National Academy of Science of Ukraine, Vernadsky Street 36, 680 Kyiv 142, Ukraine
Influence of sample thickness on the parameters of martensitic transfonnations and microstructure peculii-, ities of martensite in splat quenched with rate 104 -106 K/s alloys Ti 50Ni 50-xCu x ( x = 5-32 at. %) has been investigated and discussed. Film thinning results in lowering of the characteristic transformation temperatures, decrease of hysteresis, change of transition intervals. Morphological peculiarities of martensite are also changed after additional thinning. Metastable phase diagram of TiNiCu system after splat quenching and after additional thinning was constructed. Influence of thinning on crystallization parameters of amorphous samples are studied. Observed influence of tlùckness is stipulated by the stress state arising during transformation in thinned samples.
© EDP Sciences 2003