Dimensional effect during martensitic transformation in splat cooled Ti$\mathsf{_{50}}$Ni$\mathsf{_{50-x}}$Cu$\mathsf{_x}$ ($\mathsf{x = 5-32}$ at. %) alloys

V. A. Lobodyuk

doi:doi:10.1051/jp4:2003987

Issue		J. Phys. IV France Volume 112, October 2003


Page(s)		735 - 738
DOI		https://doi.org/10.1051/jp4:2003987

J. Phys. IV France 112 (2003) 735
DOI: 10.1051/jp4:2003987

Dimensional effect during martensitic transformation in splat cooled Ti $\mathsf{_{50}}$ Ni $\mathsf{_{50-x}}$ Cu $\mathsf{_x}$ ( $\mathsf{x = 5-32}$ at. %) alloys

V. A. Lobodyuk

Department of Phase Transformations, G.V. Kurdyumov Institute for Metal Physics of National Academy of Science of Ukraine, Vernadsky Street 36, 680 Kyiv 142, Ukraine

Abstract
Influence of sample thickness on the parameters of martensitic transfonnations and microstructure peculii-, ities of martensite in splat quenched with rate 10⁴ -10⁶ K/s alloys Ti ₅₀Ni _50-xCu _x ( x = 5-32 at. %) has been investigated and discussed. Film thinning results in lowering of the characteristic transformation temperatures, decrease of hysteresis, change of transition intervals. Morphological peculiarities of martensite are also changed after additional thinning. Metastable phase diagram of TiNiCu system after splat quenching and after additional thinning was constructed. Influence of thinning on crystallization parameters of amorphous samples are studied. Observed influence of tlùckness is stipulated by the stress state arising during transformation in thinned samples.

Dimensional effect during martensitic transformation in splat cooled Ti Ni Cu ( at. %) alloys

Dimensional effect during martensitic transformation in splat cooled Ti $\mathsf{_{50}}$ Ni $\mathsf{_{50-x}}$ Cu $\mathsf{_x}$ ( $\mathsf{x = 5-32}$ at. %) alloys