Shock Behaviour of 3D Carbon-Carbon Composite

P.-L. Héreil1, O. Allix2 and M. Gratton2

1  Centre d'Études de Gramat, 46500 Gramat, France
2  École Nationale Supérieure d'Enseignement Technique, 92000 Cachan, France


Abstract
The compressive response of a 3D carbon-carbon composite under shock wave was studied in a plate-impact configuration. Two directions of impact were achieved until a nominal value of longitudinal stress of 2.5 GPa. The measured wave profiles are consistent with previous results on 3D composites and confirm the behaviour of such materials under impact. It is shows that the initial loading is decomposed in two waves. The first one is transmitted by the longitudinal fibres, the second one corresponds to the propagation of a shock wave in the 'matrix'. Macroscopic characteristics of this material are provided.


Résumé
On présente la réponse sous choc d'un composite 3DCC à partir d'essai d'impact de plaques. Deux directions d'anisotropie ont été étudiés jusqu'à une contrainte maximum de 2,5 GPa. La forme des diagrammes de vitesse est cohérente avec les résultats déjà obtenus sur les composites 3D et confirme leur comportement sous choc. On montre que la sollicitation initiale se décompose en deux ondes. La première est transportée par les fibres longitudinales, la seconde par la matrice. On présente des caractéristiques macroscopiques calculées sur ce composite 3DCC.