Influence of Temperature and Strain Rate on the Mechanical Behavior of Adiprene L-100
G.T. Gray III, W.R. Blumenthal, C.P. Trujillo and R.W. Carpenter IIMaterials Research and Processing Science, Los Alamos National Laboratory, Los Alamos NM 87545, US.A.
Abstract
The effect of sample thickness, strain rate, and temperature on the mechanical response of Adiprene-L100 is presented. The compressive stress-strain response of Adiprene-L100 was found to depend on both the applied strain rate ; [MATH], and the test temperature at high-rate ; [MATH]. Due to the slow, dispersive wave propagation in Adiprene-L100, thinner sample thicknesses are needed to assure uniform, uniaxial stress conditions within Hopkinson Bar samples ; the optimal sample thickness being dependent on test temperature. Decreasing temperature from 298 to 77K at 3000 s-1 was found to increase the maximum flow stress in Adiprene-L100 from 10 to ~210 MPa.
Résumé
Nous présentons l'influence de la vitesse de déformation, [MATH], de la température d'essai, T, et de l'épaisseur de l'échantillon sur le comportement mécanique sous grandes vitesses de sollicitation de 1'Adiprene-L100 : sa réponse en compression dépend à la fois de [MATH] et de T. À cause de la nature dispersive de la propagation des ondes dans l'Adiprene-L100, les épaisseurs des échantillons doivent être faibles pour assurer un état de contrainte uniforme dans l'éprouvette ; l'épaisseur optimale dépend de la température d'essai. À 3000 s-1, une décroissance de T, de 298 à 77K, entraîne une augmentation de la limite d'écoulement maximale de 10 à ~210 MPa.