High Speed Tensile Testing

I.H. Hove; B. Andersson; T.E. Johnsen

doi:doi:10.1051/jp4:1997341

Numéro		J. Phys. IV France Volume 07, Numéro C3, August 1997 EURODYMAT 1997 - 5th International Conference on Mechanical and Physical Behaviour of Materials under Dynamic Loading


Page(s)		C3-229 - C3-234
DOI		https://doi.org/10.1051/jp4:1997341

EURODYMAT 1997 - 5th International Conference on Mechanical and Physical Behaviour of Materials under Dynamic Loading

J. Phys. IV France 07 (1997) C3-229-C3-234
DOI: 10.1051/jp4:1997341

High Speed Tensile Testing

I.H. Hove, B. Andersson and T.E. Johnsen

Forskingsveien I, Dept of Casting and Metal Forming, SINTEF, P.O. Box 124 Blindern, 0314 Oslo, Norvège

Abstract
The experimental method of the testing at a high speed machine with ram speed of l-l0m/s is described. The reproducibility and the effects of the material and the ram speed on the oscillations in measured load have been studied. A software for subtracting the oscillations, which seem to come mainly from the load measurements system, from the recorded load signal to get the material response has been developed. By our method the time from a sample is mounted to the results from the test is ready is about 20 min. Aluminium (3005) and steel have been tested both at high speed and at conventional speed. The mechanical properties as function of strain rate are found.

Résumé
Cet article décrit la méthode expérimentale utilisée pour un test sur une machine de traction à grande vitesse dont la vitesse ram est de 1-10 m/s. La reproductibilité. les effets dus au materiau et à la vitesse ram sur les oscillations sous contrainte ont été étudiés. Un programme a été développé pour soustraire du signal de contrainte enregistré les oscillations provenant principalement du système de mesure sous contrainte afin d'obtenir la réponse du matériau. A l'aide de cette méthode. le temps utilisé entre en mise en place de l'échantillon et les résultats du test se réduit à 20 min.