Scaling Effects in Penetration : A Taylor Test Approach
J.U. Cazamias and S.J. BlessInstitute for Advanced Technology, 4030-2 West Braker Lane, Austin, TX 78759, U.S.A.
Abstract
Taylor Tests with L/D = 5 rods (1 cm and 0.2 cm in
diameter) were conducted on armor steel (RHA) at 215 to 280 m/s to examine
scale effects. AUTODYN-2D calculations confirmed dimensional analysis which
predicts that strain rate should scale inversely with size. Yield strengths
(Yd) determined from the Wilkins-Guinan formula were found to be 7
to 9% greater in the smaller specimens which is a little less than the 12%
increase predicted from a logarithmic dependence of strength on strain
rate.
Résumé
Nous avons effectué des Tests de Taylor pour des
échantillons cylindriques d'acier RHA (rapport L/D = 5, D = 1 cm et 0.2 cm)
pour des vitesses allant de 215 à 280 m/s afin d'étudier les effets d'échelle.
Des simulations numériques avec AUTODYN-2D ont confirmé l'analyse dimensionelle
qui prédit une vitesse de déformation inversement proportionelle au diamètre.
Nos résultats montrent que la contrainte d'écoulement, déterminée à partir de
la formule de Wilkins-Guinan, est 7 à 9% plus grande pour les petits
échantillons. Ces valeurs sont proches des 12% d'augmentation prédits par une
dépendance logarithmique de la contrainte en fonction de la vitesse de
déformation.