Ductile to Brittle Transition Fracture Behaviour of Ductile Steel at High Strain Rates

Abstract
320x75x18mm 3 point bend specimen have been subjected to impact testing. The material was a micro alloyed structural steel of three different heat treatment qualities. The micro structure consisted of layers of perlite in a ferrite matrix. The experiments were performed at 30 and 45m/s. Depending on load rate the fracture was ductile, brittle or in a mixed mode. Simulations of the experiments showed strain rates of 10³ to 10⁴. At low impact velocity some specimen could withstand the initial load without failing. A maximum likelihood model are used to fit the specimen behaviour to the experimental data.

Résumé
Des spécimens 320x75x18mm avec 3 points de flexion étaient soumises à une expérience d'impact. Le matériau était en micro allie acier de trois différent qualités de traitement de chaleur. Les expériences étaient conduites à 30 et 45m/s. Selon la vitesse de la force d'impact, la fracture était ductile, fragile, ou d'une façon intermédiaire. Les simulations des expériences montraient une vitesse de déformation de 10³ jusqu'à 10⁴. À une basse vitesse de l'impact quelque spécimen pouvait supporter la force initiale sans ruine.