Stabilisation des phases monocristallines quadratique et cubique dans BaTiO₃

Abstract
Single crystals of Ba Yb_xTiO₃ and Ba Sr_xTiO₃ with tetragonal structure were grown by the floating zone (FZ) method using an LHPG (Laser Heated Pedestal Growth) technique. The grown crystals, typically 1 mm in diameter and 8 mm in length, were yellowish transparent. Substitution of more than 2.5 at % Sr for Ba in BaTiO3 and addition of 3 to 5 at % Ln (Ln= Yb, Eu), were effective in preventing the formation of the hexagonal phase. The Eu³⁺ emission spectra recorded at room temperature demonstrate a significant intensity enhancement of the ⁵D₀ -> ⁷F₁ magnetic dipolar transition compared to the ⁵D₀ -> ⁷F₂ electric dipolar transition.

Résumé
Les fibres monocristallines de Ba Yb_xTiO₃ et Ba Sr_xTiO₃ de structure quadratique ont été préparées par la méthode de la zone flottante (FZ) en utilisant la technique LHPG (Laser Heated Pedestal Growth). Les échantillons élaborés, de dimensions 1mm x 8 mm, sont jaunâtres et transparentes. La substitution du baryum par plus de 2,5 mol% de Sr dans BaTiO₃ et le dopage de 3 à 5 mol% de Ln (Ln = Yb, Eu) évitent la formation de la phase hexagonale. Le spectre d'émission de Eu³⁺ enregistré à température ambiante montre le changement de structure traduit par la forte intensité de la transition dipolaire magnétique ⁵D₀ -> ⁷F₁ comparée à celle de la transition dipolaire électrique ⁵D₀ -> ⁷F₂.