Étude des équilibres des phases dans le système Ag-Sn-In à 280 °C

Abstract
The Ag-Sn system is among the most studied ones in the prospective of the abandon of the lead containing alloys. On the other hand the temperatures of these alloys are higher than those of the now used Pb-Sn eutectic alloys. Consecutively the addition of In - a low melting element is interesting from the new materials' development. The isothermal section of the Ag-Sn-In system at 280°C was studied by using optical and scanning electron (SEM) microscopies, X-ray diffraction, differential scanning calorimetry (DSC) and Vickers' microhardness measurements. The microhardness values of (Ag), (Ag₄Sn) and phases were measured. The ternary eutectic's position reported in the literature was confirmed. The respective third element's solubilities were determined.

Résumé
Le système Ag-Sn est parmi les systèmes les plus étudiés dans la perspective de l'abandon des alliages à base de Pb. D'autre part les températures de fusion de ces alliages sont plus élevées que celle de l'eutectique Pb-Sn actuellement employé. Consécutivement, l'addition d'indium, un élément ayant température de fusion relativement basse, est un moyen intéressant pour la mise au point de nouvelles brasures. La coupe isotherme du système Ag-Sn-In à 280°C a été construite à l'aide des microscopies optique et électronique à balayage (MEB), de la diffraction des rayons X, de mesures de microdureté Vickers et de calorimétrie différentielle à balayage (DSC). Les microduretés des phases (Ag), (Ag₄Sn) et ont été mesurées. La position de l'eutectique ternaire rapportée antérieurement dans la littérature a été confirmée. Les solubilités du troisième élément respectif ont été déterminées.