Impact Fracture Testing of Engineering Polymers (Part 2)

Abstract
To characterize the dynamic fracture behaviour of high density poly(ethylene) (PE-HD) and poly(oxy-methylene) (POM), instrumented impact tests were performed with a servohydraulic test system using various specimens under bending and tensile loading. The objectives of this study were to develop and implement a test methodology and a data recording and reduction scheme for various test speeds and impact rates (0.001 to 8 m/s), and to determine the effect of the impact rate on the fracture toughness of PE-HD and POM. The data reduction to determine dynamic fracture toughness values was carried out according to different procedures taking account of the specific impact rates and the deformation behaviour of the materials tested.

Résumé
Pour caractériser le comportement de rupture aux grandes vitesses de polyéthylène de haute densité (PE-HD) et polyoxyméthylène (POM), on a fait des essais d'impact instrumentés avec une machine d'essai servo-hydraulique avec des spécimens divers sous flexion et traction. Les objectifs de ces études étaient le dévelopment et l'implémentation d'une méthodologie d'essai et un schéma d'acquisition et réduction des données pour des vitesses d'essai différents (de 0.001 a 8 m/s), et la détermination de l'effet de la vitesse d'impact sur le facteur critique d'intensité des contraintes, K_Ic de PE-HD et POM. La réduction des données pour évaluer K_Ic a été réalisée en prenant les vitesses d'impact spécifiques et le comportement de déformation des matériaux testés en considération.