| Issue |
J. Phys. IV France
Volume 06, Number C8, Décembre 1996
ICIFUAS 11Eleventh International Conference on Internal Friction and Ultrasonic Attenuation in Solids |
|
|---|---|---|
| Page(s) | C8-385 - C8-388 | |
| DOI | https://doi.org/10.1051/jp4:1996882 | |
ICIFUAS 11
Eleventh International Conference on Internal Friction and Ultrasonic Attenuation in Solids
J. Phys. IV France 06 (1996) C8-385-C8-388
DOI: 10.1051/jp4:1996882
Department of Materials Science, Iwaki Meisei University, Iwaki, Fukushima 970, Japan
© EDP Sciences 1996
Eleventh International Conference on Internal Friction and Ultrasonic Attenuation in Solids
J. Phys. IV France 06 (1996) C8-385-C8-388
DOI: 10.1051/jp4:1996882
Internal Friction of Metastable Austenitic Stainless Steel SUS 301
I. YoshidaDepartment of Materials Science, Iwaki Meisei University, Iwaki, Fukushima 970, Japan
Abstract
Anelastic measurements in the low frequency range have been made on a nickel reduced type metastable austenitic stainless steel SUS 301. Cold working of various degrees was given by rolling after austenitizing heat treatment. Three internal friction peaks, P1, P2, P3 from the lower temperatures, were obsewed. The sharp peak P2 and the broad one P3 disappeared by austenitization and reappeared by cold rolling. Peak P2 was a single relaxation type with an activation energy of about 0.5 eV. Electrical resistivity and thermopower were measured ; it was revealed that the latter was more sensitive to the martensitic transformation than the former.