Germination et texture du composé supraconducteur Nb ₃Sn

Abstract
The composite design and/or manufacturing process of the Nb ₃Sn multifilamentary strands are continuously changed so as to improve the superconducting behaviour. Such an enhancement depends on both the amount and microstructure of the superconducting phase. The study of the parameters and of the mechanisms of the phase transformations is therefore of the higher importance. The stages of nucleation and growth of the Nb ₃Sn grains are mainly investigated by thin foil transmission electron microscopy and by X-ray diffraction. The results obtained with the various techniques are shown to be in accordance and to complete each other. An example establishes their usefulness in order to explain the evolution of the critical current density. The effect of the grain misorientation on the critical current density is also considered.

Résumé
L'amélioration du comportement supraconducteur des composites multifilantentaires à base de Nb ₃Sn passe par la définition de nouveaux designs et/ou de nouveaux procédés de fabrication. Le comportement supraconducteur est régi par la quantité et la microstructure de la phase supraconductrice. Ce dernier paramètre impose d'identifier la nature des mécanismes des transformations de phases et leurs paramèt res. La démarche met en oeuvre la microscopie électronique en transmission et la détermination des orientations cristallographiques aux rayons X. Elle est appliquée aux stades de germination et de croissance des grains de la phase Nb ₃Sn dans le procédé de la source d'étain interne. Les apports complémentaires et concordants des différentes techniques sont dégagés. L'importance des résultats pour l'interprétation des variations de la densité de courant critique est démontrée par un exemple. L'influence de la désorientation entre les grains sur la densité de courant critique est finalement considérée.