Thermomechanical Properties of Polycrystalline Vanadium in Compression

Abstract
The mechanical behavior of commercially pure polycrystalline vanadium (99.8%) has been characterized in compression over a strain rate range of 10⁴ to 6x10³ s^-1. In addition, the temperature dependence of the flow stress of vanadium has been examined over a range of temperatures from 25 to 700 °C for a strain rate of 10³ s^-1. Optical metallography of the deformed specimens revealed no twins, deformation bands or microcracks, suggesting that the deformation proceeded largely by crystallographic slip. The strain rate and temperature dependence of the strain hardening rate and flow stress is indicative of a BCC material, although a pronounced local peak in the flow stress was observed at about 400 °C.

Résumé
Le comportement mécanique de polycristaux de Vanadium (pureté commerciale : 99,8%) a été caractérisé en compression pour des taux de déformation allant de 10⁴ à 6.10³ s^-1. L'évolution de la limite d'élasticité en fonction de la température a par ailleurs été analysée sur une plage de 25 à 700 °C. L'observation en microscopie optique des échantillons déformés a montré l'absence de mâcle, de bande de déformation ou de micro-fissure, ce qui suggère un mode de déformation par glissement cristallographique. A l'exception d'une anomalie de limite élastique vers 400 °C, le taux de déformation et l'évolution de la limite d'élasticité en fonction de la température est caractéristique des métaux cubiques centrés.