Numéro |
J. Phys. IV France
Volume 06, Numéro C8, Décembre 1996
ICIFUAS 11Eleventh International Conference on Internal Friction and Ultrasonic Attenuation in Solids |
|
---|---|---|
Page(s) | C8-89 - C8-92 | |
DOI | https://doi.org/10.1051/jp4:1996817 |
ICIFUAS 11
Eleventh International Conference on Internal Friction and Ultrasonic Attenuation in Solids
J. Phys. IV France 06 (1996) C8-89-C8-92
DOI: 10.1051/jp4:1996817
1 Universidad Nacional de Rosario, Departamento de Física, Avda. Pellegrini 250, 2000 Rosario, Argentina
2 Departamento de Física de la Materia Condensada, Facultad de Ciencias, Universidad del País Vasco, Apdo. 644, 48080 Bilbao, Spain
3 Laboratorio de Espectroscopía Mecánico Dinámica, Instituto de Física Rosario (IFIR-CONICET-UNR), Avda. 27 de febrero 210 bis, 2000 Rosario, Argentina
4 Instituto de Física, Universidad Católica de Valparaíso, Avda. Brasil 2950, Valparaíso, Chile
© EDP Sciences 1996
Eleventh International Conference on Internal Friction and Ultrasonic Attenuation in Solids
J. Phys. IV France 06 (1996) C8-89-C8-92
DOI: 10.1051/jp4:1996817
Activation Parameters of the Zener Peak in Cu-Li Alloys Produced by Electrodeposition
O.A. Lambri1, 2, A. V. Morón-Alcain3, E.D. Bulejes3, A. Penaloza4 and M. Ortiz41 Universidad Nacional de Rosario, Departamento de Física, Avda. Pellegrini 250, 2000 Rosario, Argentina
2 Departamento de Física de la Materia Condensada, Facultad de Ciencias, Universidad del País Vasco, Apdo. 644, 48080 Bilbao, Spain
3 Laboratorio de Espectroscopía Mecánico Dinámica, Instituto de Física Rosario (IFIR-CONICET-UNR), Avda. 27 de febrero 210 bis, 2000 Rosario, Argentina
4 Instituto de Física, Universidad Católica de Valparaíso, Avda. Brasil 2950, Valparaíso, Chile
Abstract
Copper-lithium alloys were produced by electrodeposition. They show a Zener peak at 650 K (at 0.2 s-1) which appears overlapped with the low and intermediate temperature grain boundary damping peaks of copper and also with the phase transition peak related to Cu-18 at% Li crystals. In this work the activation energy, H, and the pre-exponential factor τo were calculated. Those were H = ( 160 ± 4) KJ/mol and τo = 2 x 10 (-14 ± 1) (s).