CHANGEMENTS DE PHASES ET MICROSTRUCTURES
J. Phys. IV France 04 (1994) C3-243-C3-250
Transformations microstructurales lors de la mécanosynthèse de l'alliage Ti-47.5A1-3CrV. JACOB1, J. MISHURDA2, A. FREFER2, R. BACCINO1, F. MORET1, C. SURYANARAYANA2 and F.H. FROES2
1 CEREM/Laboratoire de Génie des Matériaux, CENG 85X, 38041 Grenoble cedex, France
2 IMAP/College of Mines & Earth Resources, University of Idaho, Moscow, Idaho 83843-4195, U.S.A.
Mechanical milling of pre-alloyed Ti-47.5AI-3Cr (at.%) powder has been carried out in a vibratory mill. The microstructural evolution of the materials was studied as a function of milling time. An ultrafine microstructure was produced with a crystallite size of about 15 nm and a partial amorphization was obtained after 2 hours of milling.