Investigation of Dynamic Crack Propagation and Arrest for Pulse Loaded specimens Made from a Modified MoV-Steel (KS22) by Means of a Hopkinson-Pressure-Bar
K. Kussmaul and U. MayerStaatliche Materialprüfungsanstalt (MPA) University of Stuttgart, Pfaffenwaldring 32, 70569 Stuttgart, Germany
Abstract
Experimental and numerical investigations on crack initiation under transient loading, crack propagation behaviour and crack arrest of 17 MoV 84 (mod.) using fracture mechanics methods are described. Results of Split-Hopkinson-bar-tests using a single-specimen method and a high-speed camera are compared with multi specimen results and values obtained from other specimens and load velocities.
Résumé
Ce rapport décrit des études expérimentales et numériques concernant l'initiation des fissures sous charge transitoire, ainsi que leur propagation et arrêt dans le matériau 17 MoV 84 (mod.) en utilisant des méthodes de mécanique de fracture. Les résultats des essais Hopkinson avec une méthode à une éprouvette et une caméra à action rapide ont été comparés à ceux obtenus avec plusieurs éprouvettes et aux valeurs d'autres éprouvettes et d'autres vitesses de charge.