Material Characterization Tests and Modelling of Carbon Fibre T300/914 at Impact Rates of Strain
S.R. Hallett and C. RuizDepartment of Engineering Sciences, University of Oxford, Parks Road, OX1 3PJ Oxford, U.K.
Abstract
This paper describes a series of tests which were conducted in order to obtain material and rate dependance data for carbon fibre T300/914. The results show there to be only a small amount of rate dependance. The information gained from the tests was then used as input data for the finite element code, DYNA-3D, in order to attempt to model the failure which occurred. Results have shown good predictions for initiation of damage but are not sufficient for delamination prediction of damage growth.
Résumé
Cette publication décrit une série de tests qui ont été conduit afin d'obtenir des données sur la dépendance du taux de contrainte des fibres de carbone T300/914. Les résultats montrent qu'il n'existe qu'une faible dépendance. Les résultats obtenus à partir de ces tests ont ensuite été introduits dans un code à éléments finis, DYNA-3D, afin d'essayer de modéliser la fracture. Les résultats sont en bon accord concernant l'initiation de la fracture mais restent insuffisants pour prévoir la croissance des dommages par délaminage.