The Effect of Strain Rate on the Compressive Stress-Strain Properties of PEEK and Epoxy Carbon Fibre Composites
D.J. ParryDepartment of Physics, Loughborough University, Loughborough, Leicestershire LE11 3TU, U.K.
Abstract
The dynamic compressive behaviour of two AS4 carbon fibre composite systems has been studied at room temperature at strain rates from about 10-3 s-1 103 s-1. One system (APC2) had a thermoplastic PEEK matrix, while the other system (EC) had a thermoset epoxy resin matrix. Transverse unidirectional and transverse cross-ply fibre configurations were used for each system. Both configurations showed greater stiffness, linearity and strength at high rates than at low rates, but the high rate behaviour of the APC2 was more complex than that of the EC. The measured Young's modulus values were in good agreement with theoretical predictions.
Résumé
Le comportement sous pression dynamique de deux systèmes de AS4 fibre de carbon transversal a été étudié à température ambiante, entre des vitesses de déformation de 10-3 s-1 j'usqu'à 103 s-l . Un composite APC2 avait une matrice PEEK, tandis que l'autre EC avait une matrice de résine époxyde. A des vitesses de deformation élevées les deux composites ont montrés plus de rigidité, linéairité et resistance, mais le comportement du APC2 à vitesse de déformation elevée était plus compliqué que celui du EC. Les valeurs mesurées du module de Young étaient en bon accord avec les prédictions théoriques.