Décomposition de la phase β-métastable de l'alliage de titane β-Cez au cours du chauffage et du recuit

R. SANGUINETTI, M. ZANDONA, A. PIANELLI and E. GAUTIER

Laboratoire de Science et Génie de Matériaux Métalliques, URA 159 du CNRS, Ecole des Mines, Parc Saurupt, 54042 Nancy cedex, France


Abstract
This work carries out the study of the precipitation during continuous heating up to 830°C and ageing at this same temperature from β meta + w aniso or β meta + α. The heating rates varied between 0.25 and 5°C/s. The transfomations were followed by electric resistivity and hardness measurements. Different samples were quenched from different temperatures during the heating range and were then studied by X-ray and TEM. The beginning temperatures of precipitations of the w and α phases were established, as the continuous heating transformation diagrams. Near 700°C, X-ray quantitative analysis and EAM studies revealed ( for quenching and 4.5°C/s cooling rate) that the structure consisted of a maximum content of the α phase, surrounded by β zones enriched in Fe, Cr. For temperatures greater than 700°C, the content of the α phase diminished and the β phase composition was homogenized.