EDP Sciences Journals List
Issue J. Phys. IV France
Volume 03, Number C9, Décembre 1993
Proceedings of the 3rd International Symposium on High Temperature Corrosion and Protection of Materials
Actes du 3ème Colloque International sur la Corrosion et la Protection des Matériaux à Haute Température
Page(s) C9-521 - C9-529
DOI http://dx.doi.org/10.1051/jp4:1993955

Proceedings of the 3rd International Symposium on High Temperature Corrosion and Protection of Materials
Actes du 3ème Colloque International sur la Corrosion et la Protection des Matériaux à Haute Température

J. Phys. IV France 03 (1993) C9-521-C9-529

DOI: 10.1051/jp4:1993955

High temperature corrosion study on yttrium modified aluminide coatings on IN 713C

Kyoo Young Kim, Jae Ho Jun and Jae Kee Lee

Dept. of Materials Science and Engineering, Pohang Institute of Science and Technology and Research Institute of Industrial Science and Technology, P. O. Box 125, Pohang 790-600, Korea


Abstract
The addition of active elements in high temperature materials may improve corrosion resistance extensively. In general, the active elements are incorporated in the form of an alloying element either in the bulk or in overlay coatings, as an oxide dispersion, or by ion implantation. In this experiment, yttrium was incorporated by an ion plating method either before or after pack aluminizing to maximise the corrosion resistance of IN 713C. Various combinations of pack aluminizing and yttrium ion plating were examined with respect to coating sequence, aluminium activity, and corrosion environment. From all the various coating combinations examined, the best corrosion resistance was obtained from the H/A + Y (high activity aluminizing + Y-ion plating) type multilayer coatings. Uniformity of the Y deposition was greatly dependent upon the surface condition of the aluminide coating layer. The high activity aluminide coating gave better uniformity of Y deposition than did the low activity aluminide coating. Improvement of corrosion resistance by the Y-modified aluminide multilayer coatings of H/A + Y type may occur because Y present between the A12O3 columns improves the A12O3 scale adherence and substantially prohibits depletion of Al in the aluminide coating layer.